SILIBASE SILICONE Produce Performance Comparable to SILRES MP 50 E Silicone Resin.
Apr 23, 2024
Chinese Factory of Analogue Substitute for SILRES® MP 50 E Silicone Resin
Product Name: Silicone Resin
Item No.: SilibaseSR-X860
Benefit
By utilizing silicone resin emulsion SilibaseSR-X860, a complete range of water-based high-temperature coatings can be formulated and produced while retaining all the benefits of a silicone based coating:
- High heat resistance
- Excellent adhesion
- Chemical resistance
- Corrosion resistance
SilibaseSR-X860 has good compatibility with other organic resins, which in turn, provides formulators with flexibility and enables ease of compounding during the manufacturing process.
Introduction
Our company supply analogue Similar Excellent adhesion SILRES® MP 50 E Silicone Resin.SilibaseSR-X860 is mainly used for high-temperature resistant coatings, with excellent high-temperature resistance and weather resistance; Has good flexibility and hardness, and can quickly dry at room temperature; Adding polysilazane can dry at room temperature. Suitable for blending various series of high-temperature resistant coatings, high-temperature resistant self-drying coatings, and H-grade insulation coatings, etc.
Application Suggestions:
SilibaseSR-X860 | 350 | Organic bentonite | 10 |
Copper chromium black | 130 | 560 | 20 |
High melting point glass powder | 230 | Micro silica | 55 |
Ceramic powder | 40 | Nano alumina | 20 |
Mica powder | 90 | dispersing agent | appropriate amount |
Leveling agent | appropriate amount | xylene | 100 |
Flux T18 | 15 | N-butanol | 28 |
Gas silicon | 10 | | |
800 ℃, 30 minutes, the paint film is intact without peeling or peeling, with a hardness of over 8H, good adhesion, and toughness. |
1000 ℃, 3 hours, the paint film is intact without peeling and has toughness. |
A Wide Variety of Application
Replacement product for SILRES® MP 50 E silicone resin.SilibaseSR-X860 is used in all types of coatings for oven and stove paints and for household appliances that are regularly subjected to high temperatures, such as pots, pans and toasters. Mufflers and exhaust systems on motorcycles, recre ational vehicles and automotive are some of the other more popular applications in which SilibaseSR-X860 provides high temperature protection and performance.SilibaseSR-X860 is suitable for use under recommendation XV and silicones of the BfR.
Advantages
Chinese Factory produce widely used organosilicon resins similar to SILLES ® MP 50 E.
- Excellent airdrying properties
- Tack-free after one hour at RT
- Water-based phenyl-methyl resin emulsion
- Provides water-based paints with high thermal stability
- Good compatibility with organics
- BfR XV confirmed
- Broad end use application range
Technical data:
Parameters
| Test conditions
| Index
|
Exterior | Visualization | Colorless or light-yellow transparent liquid, allowing for trace amounts of milky color, without mechanical impurities |
Solvent | / | Xylene, n-butanol |
Solid content% | 150℃,2 h | 50±2 |
Viscosity·mPa. s (cps) | Rotational Viscometer（NDJ9S) 25℃ | 60-200 |
Table drying time | Horseshoe iron sheet25℃ | Dry surface for 30-40 minutes |
Hardness | Drying Time250℃，30min | HB-H |
Heat resistance | Copper sheet 200 ℃ ≥ 300h (Aluminum powder paint 650 ℃, 3h) | No yellowing, no peeling |
Weightlessness | 400℃.3h | ≤5.0% |
Degree of substitution | / | 1.36 |
Phenyl/methyl ratio | / | 0.8/1.0 |
Storage and transportation precautions:
If solvent evaporation is found, it can be diluted with the corresponding solvent and continued to be used. Store in a cool and ventilated warehouse below 35℃, avoid contact with acids and alkalis, and keep away from sparks and heat sources. There should be fire protection equipment level fire exits, which should be handled with light loading and unloading. According to the storage and transportation of dangerous goods.
Shelf life:
12 months