Glass fiber reinforced plastic: Improve thephysical and mechanical strength of the composite wet, wet electricalperformance, and improve the glass fiber cluster, protection and processingtechnology.Adhesives and coatings: Improve the wetadhesion, weatherability, improve pigment dispersion, improve wear resistanceand resin crosslinking.Casting: Improve the strength of resinsand. To achieve a high degree of low gas evolution.Rubber: Improve product mechanicalstrength, wear resistance, wet electric ...

Coupling agent is very common in our liveschemical raw materials. In plastic compounding, the coupling agent is toimprove the synthetic resin and inorganic filler or reinforcing materialinterface properties of a plastic additive, coupling agent, also known assurface modifier. It can reduce the viscosity of synthetic resin melt in theplastic processing, improve the dispersion of filler to improve the processingperformance, thus enabling the products to obtain good surface quality andmechanical, t ...

Trichlorosilaneis an important synthesis of organic silicon intermediates, but also the preparationof semiconductor grade polysilicon and solar cell grade polysilicon of the mainraw materials. For a longtime, due to China's smaller production capacity of polysilicon,trichlorosilane is mainly used for organic silicone rubber coupling agent andother silicone materials, the amount of polysilicon is very small.Hydrogenchloride method: the method is to use metallurgical grade silicon powder as rawmat ...

For the surface treatmentof glass fiber. Silane coupling agent can improve theglass fiber and resin adhesive properties, improve the glass fiber reinforcedcomposite material strength, water resistance, weather resistance and otherproperties. In 2004 the use of glass fiber silane coupling agentaccounts for about 50% of the total consumption, which used more varieties ofvinyl silane, aminosilane, methacryloxysilane and so on.For surface treatment ofinorganic fillers. Silane coupling agent In thein ...

Silane coupling agent is a kindof special structure of low molecular weight organic silicon compounds. The general formula for RSiX3, where R representsamino, mercapto vinyl, epoxy, chloropropyl, cyano and methacryloxy groups andother groups. These groups and different matrixresins have a strong ability to react, and x represents a hydrolyzable groupsuch as halogen, alkoxy, acyloxy and the like. Silane couplingagent is trichlorosilane (HSiCl3) and with reactive groups of unsaturatedolefins in th ...

Theaction of the defoamer is to suppress and eliminate the generation of airbubbles. In general, when the viscosity of water-based ink is toohigh, PH value is low, or when the press speed is relatively fast when it iseasy to produce bubbles, if the amount of bubbles will appear larger than thedirty version. Water-based inks generally usealkali-soluble binder, the binder material is an acidic resin alkali solution. Itis an aqueous solution similar to soap, because water-soluble binders have soapc ...

Roller coating test method is very close to the actualcoating construction conditions, so that different defoamers can distinguishthe role played by. Youcan even try out the amount of added. In the roller coating test, a porous sponge roller pad, the 40grams of paint on the substrate is not adsorbed, can be a dedicated test cardcan also be other standardized test paper jam. The total coating area was 500 cm2. Before each test, therollers were wetted with the same amount of water to ensure reprod ...

The flow-through test can be used to evaluate thecompatibility and defoaming effect of the defoamer with the coating systembeing tested. The samplesubjected to the stirring test was immediately poured onto a polyester film. Polyester film to be placed in avertical tilt angle of 25 degrees on the frame. Carefully observe the flow smears, showing the presence ofbubbles. The method canalso evaluate the defoaming effect of the defoamer by observing the dry film. In some cases, extremely high levels ...

The effectiveness of defoamers must first be determined inthe laboratory. Itis not advisable to transfer lab test results to production scale withoutfurther testing. Ourwork in the test method developed, combined with the paint manufacturing andconstruction process conditions, the defoamer Gongjiao evaluation is feasible. Different test methods can be selectedaccording to different construction conditions (such as brushing, spraying,dipping, printing, etc.).Stirring testFor our users, the simple ...

The amount and effectiveness of thedefoamer depends on the formulation system of the coating or ink, in particularthe type of polymer, the pH, the amount of pigment used, and the chemicalstructure of the other adjuvants used. Similarly, the manufacturing process and construction process onthe type and amount of defoamers are also required.The addition of a method to distinguishdefoamer products from defoamer emulsions and defoamer concentrates isdiscussed. Defoamers Emulsiondroplets of emulsion ...